Forums
New posts
Search forums
What's new
Articles
Latest reviews
Author list
Classifieds
Log in
Register
What's new
Search
Search
Search titles and first posts only
Search titles only
By:
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Rifles, Reloading, Optics, Equipment
Suppressors
Submitted form 1 *UPDATE: approved!!
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="Bob Wright" data-source="post: 2878783" data-attributes="member: 104363"><p>Yes, and aluminum heat treat starts fading at a low sustained temperatures. It was always a concern with products we made that required secondary processes that would hit annealing temperatures after heat treat. That could be 250F for hours of time or 350F for less. Time at temp is the variable. You'd be better off with aged stainless or titanium.</p></blockquote><p></p>
[QUOTE="Bob Wright, post: 2878783, member: 104363"] Yes, and aluminum heat treat starts fading at a low sustained temperatures. It was always a concern with products we made that required secondary processes that would hit annealing temperatures after heat treat. That could be 250F for hours of time or 350F for less. Time at temp is the variable. You'd be better off with aged stainless or titanium. [/QUOTE]